鋳造用金銀パラジウム合金の熱処理条件に関する研究
https://mdu.repo.nii.ac.jp/records/142
https://mdu.repo.nii.ac.jp/records/142dfdfbcc0-91ce-4f3f-96f7-8e20408d81b5
| 名前 / ファイル | ライセンス | アクション |
|---|---|---|
matsumoto_shigaku_01-01-07.pdf (2.1 MB)
|
|
| Item type | Journal Article(1) | |||||||
|---|---|---|---|---|---|---|---|---|
| 公開日 | 2012-05-23 | |||||||
| タイトル | ||||||||
| タイトル | 鋳造用金銀パラジウム合金の熱処理条件に関する研究 | |||||||
| 言語 | ||||||||
| 言語 | jpn | |||||||
| 資源タイプ | ||||||||
| 資源タイプ識別子 | http://purl.org/coar/resource_type/c_6501 | |||||||
| 資源タイプ | journal article | |||||||
| その他（別言語等）のタイトル | ||||||||
| その他のタイトル | Studies on Various Age-hardening Treatments for Au-Pd-Cu-Ag System Alloy | |||||||
| 著者 |
伊藤, 充雄
× 伊藤, 充雄
|
|||||||
| 抄録 | ||||||||
| 内容記述タイプ | Abstract | |||||||
| 内容記述 | The relation of the microstructure to mechanical properties had been studied on Au-Pd-Cu-Ag system alloy treated under various theremal conditions. In this report, they are made distinctly. 1. On the alloy, it was concluded to cause the transformations at 300℃, 430℃ and 680℃ by differential dilato-meter. The effect of age-hardening treatment was obtained by heating from 300 to 400℃. 2. The hardness of the specimen heating at high temperature after solid solution treatment, was indicated that maximun of hardness was Hv 276 under the high temperature microvickers hardness tester at 350℃ and 400℃ but that as-cast was decreased as heating. 3. The maximun of mechanical strength was obtained by heat-treatment at 350℃ for 60 min. after solid solution treatment at 800℃. The maximum value was tensile strength of 94kg/mm^2, bending strength of 115kg/mm^2, and Hv 294. 4. The bending stength was influenced by thickness of specimens. 5. The microstructure of as-cast specimen was observed to vary, heating above 500℃ by the high temperature microscope, but that in the spesimen treated solid solution some acicular precipitaties were appeared in the grain and they were disappeared at above 700℃. 6. The most of the precipitates was observed on the microstructure of specimen heated at 350℃ after solid solution treatment at 800℃. | |||||||
| 書誌情報 |
松本歯学 巻 1, 号 1-2, p. 22-29, 発行日 1975-12-31 |
|||||||
| 出版者 | ||||||||
| 出版者 | 松本歯科大学学会 | |||||||
| 書誌レコードID | ||||||||
| 収録物識別子タイプ | NCID | |||||||
| 収録物識別子 | AN00232590 | |||||||
| フォーマット | ||||||||
| 内容記述タイプ | Other | |||||||
| 内容記述 | application/pdf | |||||||
| 著者版フラグ | ||||||||
| 出版タイプ | VoR | |||||||
| 出版タイプResource | http://purl.org/coar/version/c_970fb48d4fbd8a85 | |||||||